ot dip galvanized pipe is to make molten metal and iron matrix reaction to produce an alloy layer, so that the matrix and coating are combined. Hot dip galvanized steel pipe is first pickling, in order to remove iron oxide on the surface of the steel pipe, after pickling, through ammonium chloride or zinc chloride aqueous solution or ammonium chloride and zinc chloride mixed aqueous solution tank for cleaning, and then into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life. Hot dip galvanized steel tube matrix and molten bath have complex physical and chemical reactions, forming corrosion resistant structure of tight zinc-iron alloy layer. The alloy layer is integrated with pure zinc layer and steel tube matrix, so it has strong corrosion resistance.

ot dip galvanized pipe is to make molten metal and iron matrix reaction to produce an alloy layer, so that the matrix and coating are combined. Hot dip galvanized steel pipe is first pickling, in order to remove iron oxide on the surface of the steel pipe, after pickling, through ammonium chloride or zinc chloride aqueous solution or ammonium chloride and zinc chloride mixed aqueous solution tank for cleaning, and then into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life. Hot dip galvanized steel tube matrix and molten bath have complex physical and chemical reactions, forming corrosion resistant structure of tight zinc-iron alloy layer. The alloy layer is integrated with pure zinc layer and steel tube matrix, so it has strong corrosion resistance.

ot dip galvanized pipe is to make molten metal and iron matrix reaction to produce an alloy layer, so that the matrix and coating are combined. Hot dip galvanized steel pipe is first pickling, in order to remove iron oxide on the surface of the steel pipe, after pickling, through ammonium chloride or zinc chloride aqueous solution or ammonium chloride and zinc chloride mixed aqueous solution tank for cleaning, and then into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life. Hot dip galvanized steel tube matrix and molten bath have complex physical and chemical reactions, forming corrosion resistant structure of tight zinc-iron alloy layer. The alloy layer is integrated with pure zinc layer and steel tube matrix, so it has strong corrosion resistance.

ot dip galvanized pipe is to make molten metal and iron matrix reaction to produce an alloy layer, so that the matrix and coating are combined. Hot dip galvanized steel pipe is first pickling, in order to remove iron oxide on the surface of the steel pipe, after pickling, through ammonium chloride or zinc chloride aqueous solution or ammonium chloride and zinc chloride mixed aqueous solution tank for cleaning, and then into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life. Hot dip galvanized steel tube matrix and molten bath have complex physical and chemical reactions, forming corrosion resistant structure of tight zinc-iron alloy layer. The alloy layer is integrated with pure zinc layer and steel tube matrix, so it has strong corrosion resistance.